The optimised crystal growth, Nano-Texture coating technology gives outstanding wear and chipping resistance.
The interface between the layers is controlled at the nano level, allowing the TOUGH GRIP layer extremely high levels of adhesion to prevent delamination.
Prevents severe damage for increased stability
By dispersing an impact stress during interrupted machining, MC6035 controls crack development and achieves a good balance between fracture and welding resistance during low speed cutting.
Reducing the effect of severe fracturing
By reducing the tensile stress in the coating layer during interrupted cutting, crack development caused by impact stress is prevented.